Influence of dislocation density of nickel on dissolution kinetics in acidic chloride electrolyte

A. D. Vasilyev

Journal of Samara State Technical University, Ser. Physical and Mathematical Sciences, no. 2 (2014), pp. 149-155

Résumé

An influence of dislocation density of nickel's anode on the density of anode current and the homogeneity of anode's dissolution along the surface in the acidic chloride electrolyte was studied. To create the dislocation density of about $10^9$ cm$^{-2}$, nickel was annealed at the temperature of $ 900~^\circ \mathrm С$ for 0.5 hour. To raise the dislocation density up to $10^{10}$ cm$^{-2}$, nickel was deformed by 15 % through forging. It was detected that an increase of dislocation density of one order of magnitude enlarged the density of anode current by several times over. An electrochemical etching of annealed nickel was occurring fairly even along the surface of sample revealing the well-formed grain structure. Dissolution of deformed nickel was uneven along the surface, and the grain structure was not discovered.

Détail

Keywords: nickel dislocation density anode current density, etching
Mots-clés : grain structure.