Description of deterioration processes: damage parameter of Y. N. Rabotnov: historical remarks, fundamental results and contemporary state

L. V. Stepanova ; S. A. Igonin

Vestnik Samarskogo universiteta. Estestvennonaučnaâ seriâ, no. 3 (2014), pp. 97-114

Résumé

In the paper the detailed review of the present-day results related to problems of continuum damage mechanics is given. The survey shows the development of ideas of Y. N. Rabotnov who together with L. M. Kachanov introduced damage and continuity variables which characterize the damage state. In the paper the recent studies in the elasticity, plasticity and creep theories accounting for damage accumulation processes are discussed.

Détail

Keywords: damage variable, continuity parameter, damage tensor, computer modelling, continuum damage mechanics.

Bibliographie

[1] Rabotnov Y. N., “On a mechanism of delayed failure”, Questions of strength of materials and structures, Akademia Nauk, M., 1959, 5–7

[2] Rabotnov Y. N., Selected works. Problems of Solid Mechanics, Nauka, M., 1991, 196 pp.

[3] Kachanov L. M., “On failure time under creep conditions”, Izvestia Akademii Nauk USSR. OTN, 1958, 26–31

[4] Rabotnov Y. N., Creep of structure elements, Nauka, M., 1966

[5] Kuna M., Finite Elements in Fracture Mechanics. Theory-Numerics-Applications, Springer, Dordrecht, 2013, 464 pp. | MR

[6] Murakami S., Continuum Damage Mechanics. A Continuum Mechanics Approach to the Analysis of Damage and Fracture, Springer, Dordrecht, 2012, 423 pp.

[7] Voyiadis G. Z., Woelke P., Elasto-Plastic and Damage Analysis of Plates and Shells, Springer, Berlin, 2008, 213 pp.

[8] Voyiadis G. Z., Kattan P. I., Damage Mechanics with Finite Elements: Practical Applications with Computer Tools, Springer, 2012, 113 pp.

[9] Zhang W., Cai Y., Continuum Damage Mechanics and Numerical Applications, Springer, Berlin, 2010, 936 pp.

[10] Kukudzhanov V. N., Computer modelling of deformation, damage and fracture of nonelastic materials and structures, MFTI, M., 2008

[11] J.-F. Wen et al., “Simulation of creep crack growth in 316 stainless steel using a novel creep-damage model”, Engng. Fracture Mechanics, 98 (2013), 169–184 | DOI

[12] Kim E.-H., Rim M.-S., Hwang T.-K., “Composite damage model based on continuum damage mechanics and low velocity impact analysis of composite plates”, Composite Structures, 95 (2013), 123–134 | DOI

[13] L. Zhao et al., “Numerical investigation of factors affecting creep damage accumulation in ASME P92 steel welded joint”, Material and Design, 34 (2012), 566–575 | DOI

[14] Stepanova L. V., “Refined calculations of the stress-strain state near the crack tip under cyclic loading in a damaged medium”, Vestnik of Samara State University, 2011, no. 83, 105–115 | MR

[15] Adylina E. M., Igonin S. A., Stepanova L. V., “On nonlinear eigenvalue problem arising from the near crack tip stress analysis in the vicinity of the fatigue growing crack”, Vestnik of Samara State University, 2012, no. 3.1(94), 83–102

[16] Riedel H., “Creep Crack Initiation and Growth”, Encyclopedia of Materials: Science and Technology, 2008, 1767–1773

[17] Volkov I. A., Korotkich Y. G., State equations for visco-elastic-plastic media with damage, Fizmatlit, M., 2008, 424 pp.

[18] Korolev I. K., Petinov S. V., Freidin A. B., “Numerical Modelling of damage accumulation anf fatigue crack growth in elastic materials”, Numerical continuum mechanics, 2:3 (2009), 34–43 | Zbl

[19] Wriggers P., Nonlinear Finite Element Methods, Springer, Berlin, 2008, 566 pp. | MR

[20] Astafjev V. I., Radayev Y. N., Stepanova L. V., Nonlinear fracture mecahics, Izd-vo “Samarskiy universitet”, 2001, 632 pp.

[21] Astafjev V. I., “On the crack growth with taking into account the plastic flow under creep conditions”, Journal of Applied Mechanics and Technical Physics, 1979, no. 6, 154–158

[22] Riedel H., “The extansion of a macroscopic crack at elevated temperature by the growth and coalescence of microvoids”, Creep in Structures, Springer, Berlin, 1981, 504–519 | DOI

[23] Cocks A. C. F., Ashby M. F., “The growth of dominant crack in a creeping material”, Scr. Metall., 16 (1982), 109–114 | DOI

[24] Astafjev V. I., “Regularitis of crack growth under creep conditions”, Izvestia Akademii Nauk USSR. Mekhanika Tverdogo Tela, 1986, no. 1, 127–134

[25] Krajcinovic D., Damage Mechanics, Elsevier Science, Amsterdam, 1996

[26] Lemaitre J. A., Course on Damage Mechanics, Springer-Verlag, Berlin, 1992 | Zbl

[27] Lemaitre J. A., Desmorat R., Engineering Damage Mechanics: Ductile, Creep, Fatigue and Brittle Failures, Springer-Verlag, Berlin, 2005

[28] Chaboche J. L., “Phenomenological aspects of Continuum Damage Mechanics”, Theoretical and Applied Mechanics, eds. P. German, M. Piau, D. Caillerie, IUTAM, 1989, 41–56 | DOI

[29] Kachanov L. M., Introduction to Continuum Damage Mechanics, Martinus Nijhoff, Dordrecht–Boston, 1986 | Zbl

[30] Astafjev V. I., Shiryaeva L. K., Damage accumulation and corrosion cracking in metals under stress, Samara State University, Samara, 1998, 123 pp.

[31] Stepanova L. V., Mathematical Methods of Fracture Mechanics, Fizmatlit, M., 2009, 336 pp.

[32] Zhao J., Zhao X., “The asymptotic study of fatigue crack growth based on damage mechanics”, Engn. Fracture Mechanics, 50:1 (1995), 131–141 | DOI

[33] Zhao J., Zhang X., “On the process zone of a quasi-static growing tensile crack with power-law elastic-plastic damage”, Intern. J. of Fracture, 108 (2001), 383–395 | DOI

[34] Astafjev V. I., Grigirova T. V., Pastuchov V. A., “Influence of continuum damage on stress distribution near a tip of a growing crack under creep conditions”, Fiziko-chimicheskay mekhanika materialov, 28:1 (1992), 5–11 | MR

[35] Astafjev V. I., Grigirova T. V., “Stress and damage distribution new the growing crack tip under creep conditions”, Izvestia Akademii Nauk USSR. Mekhanika Tverdogo Tela, 1995, no. 3, 160–166

[36] Lee S. B., Lu M., Kim J. Y., “An asymptotic analysis of a tensile crack in creeping solids coupled with cumulative damage. I: Small damage region around the crack tip”, Int. J. Solids Structures, 34:24 (1997), 3163–3178 | DOI | Zbl

[37] Lee S. B., Lu M., Kim J. Y., “An asymptotic analysis of a tensile crack in creeping solids coupled with cumulative damage. II: Small damage region around the crack tip”, Int. J. Solids Structures, 34:10 (1997), 1183–1197 | DOI | Zbl

[38] Murakami S., Hirano T., Liu Y., “Asymptotic fields of stress and damage of a mode I creep crack in steady-state growth”, Int. J. Solids Structures, 37 (2000), 6203–6220 | DOI | Zbl

[39] Murakami S., Liu Y., Mizuno M., “Computational methods for creep fracture analysis by damage mechanics”, Comput. Methods Appl. Mech. Engrg., 183 (2000), 15–33 | DOI | Zbl

[40] Stepanova L. V., Fedina M. E., “On the geometry of the totally damaged zone near the crack tip in the coupled formulation (creep-damage coupling)”, Vestnik of Samara State University, 2001, no. 2, 87

[41] Pinna Ch., Doquet V., “The preferred fatigue crack propagation mode in a M250 maraging steel loaded in shear”, Fatigue Fract. Eng. Mater. Structure, 23 (1999), 173–183 | DOI

[42] Stepanova L. V., “Eigenvalues of the antiplane-shear crack problem for a power-law material”, Journal of Applied Mechanics and Technical Physics, 49:1 (2008), 142–147 | MR | Zbl

[43] Kukudzanov V. N., “Coupled models of elastoplasticity and damage and their integration”, Izvestia Akademii Nauk USSR. Mekhanika Tverdogo Tela, 2006, no. 6, 103–135 | Zbl

[44] Mika P., “Influence of variable load on damage evolution in the plate structures”, 15th International conference on computer methods in mechanics CMM-2003, Short papers (Gliwice, 2003), 253–254

[45] Izvekov O. Y., Seliskij A. A., Krypenik A. M., “Realization of energy model of continuum fracture of brittle media in SIMULIA/ABAQUS 6.9”

[46] Izvekov O. Y., Krypenik A. M., “Solution of coupled problems of continuum fracture of termo and porous elastic media in Simulia Abaqus”

[47] Izvekov O. Y., Kondaurov V. I., “Model of porous medium with elastic cracked skeleton”, Physics of Earth, 2009, no. 4, 31–42 | MR

[48] Kondaurov V. I., Mechanics and termodynamics of saturated porous medium, MFTI, M., 2007

[49] Izvekov O. Y., Kondaurov V. I., “Scattered fracture of porous materials with brittle skeleton”, Mechanics of Solids, 45:3 (2010), 445–464

[50] Hayhurst D. R., “CDM mechanisms-based modelling of tertiary creep: ability to predict the life of engineering components”, Arch. Mech., 57 (2005), 103–132 | Zbl

[51] Voyiadjis G. Z., Kattan P. I., Advances in Damage Mechanics: Metals and Metal Matrix Composites, Elsevier, Oxford, 2006

[52] Litewka A., Lis Z., “Creep damage and creep rupture of metals”, Applied Stress Analysis, eds. T. H. Hyde et al., Elsevire, 1990, 201–210 | DOI

[53] Riedel H., Fracture at high temperature, Springer, Berlin, 1987

[54] Kondaurov V. I., Fortov V. E., Basics of termomechanics of condensed media, MFTI, M., 2002, 336 pp.